Modellation: To achieve complete flow out of wax copies the wall thickness must not be less than. 0,5 mm. Investing For casting Gialloy CB/N we recommend our phosphate bonded investment compound Gilvest HS Casting For the melting process use ceramic crucibles only. Cast as fast as possible before oxide layer is mixed with the molten mass. Cool down slowly after casting. Do not quench in water.
Gialloy CB-N is a beryllium-free nickel-based bonding alloy for the production of crowns and bridges. Gialloy CB-N should not be used in patients with known sensitization to nickel.
This product contains Nickel.
Porcelain: Before applying the ceramic fire at 960-980 °C, sandblast with 110 µm aluminum oxide and clean carefully with steam. The minimum thickness of alloy before firing porcelain is 0.2 mm. Long term cooling after firing is generally recommended.
Soldering/welding: In case of necessary corrections or repair work please use Gialloy solder or Gialloy laser wire.
Polishing: The polishing is easy due to the reduced surface hardness of the alloy.
Our casting alloy product range covers all kinds of applications in the dental laboratory. They are customized to the needs of the patient and easy to process in the dental laboratory. In order to meet the high-quality demands of technicians around the world, all our alloys are beryllium free and easy to use. The cobalt-chromium are formulated to achieve unique properties and outstanding results
Gialloy CB-N (Nickel Base Dental Alloy)
RM900.00
Modellation: To achieve complete flow out of wax copies the wall thickness must not be less than. 0,5 mm. Investing For casting Gialloy CB/N we recommend our phosphate bonded investment compound Gilvest HS Casting For the melting process use ceramic crucibles only. Cast as fast as possible before oxide layer is mixed with the molten mass. Cool down slowly after casting. Do not quench in water.
Gialloy CB-N is a beryllium-free nickel-based bonding alloy for the production of crowns and bridges. Gialloy CB-N should not be used in patients with known sensitization to nickel.
This product contains Nickel.
Porcelain: Before applying the ceramic fire at 960-980 °C, sandblast with 110 µm aluminum oxide and clean carefully with steam. The minimum thickness of alloy before firing porcelain is 0.2 mm. Long term cooling after firing is generally recommended.
Soldering/welding: In case of necessary corrections or repair work please use Gialloy solder or Gialloy laser wire.
Polishing: The polishing is easy due to the reduced surface hardness of the alloy.
Caution: Never put Gialloy in an acid bath!
In stock
Description
Our casting alloy product range covers all kinds of applications in the dental laboratory. They are customized to the needs of the patient and easy to process in the dental laboratory. In order to meet the high-quality demands of technicians around the world, all our alloys are beryllium free and easy to use. The cobalt-chromium are formulated to achieve unique properties and outstanding results
Additional information
Related Products
Super 6 Alloy (NON-PRECIOUS ALLOYS)
RM680.00 Add to cartMajor Pin-Cutter Discs
RM195.00 Add to cartDentsply Lucitone 199® High Impact Denture Resin (Large Pack)
RM890.00 Add to cart